• stainless steel balls are made of an alloy with a minimum content of carbon, sulphur, phosphorus and chrome with a special thermical treatment
• very hard
• used in blast wheel machines for surface compression, deburring and cleaning of steel plates, -profiles cast parts

Properties:

• round grid
• gray color
• hardness 40 - 55 HRC
• density 8.00 kg/dmü
• cast iron 3.8 t/mü
• reuseable 200 times

iron free, synthetic minaral blast material

• balls of chalk natron glas
• the round grid shape makes the material suitable for careful surface treatment
• water insoluble, no metallic components, non cunductive
• used for blasting of aluminum and stainless steel surfaces
• even used for building cleaning

Properties:

• round grid
• white
• hardness 5-7 Mohs
• density 2.45 kg/cmü
• cast weight 1.30 t/mü

Minimum order amount 25 kg / for order up to 975 kg price / kg

iron free, synthetic blast material

• aluminum oxide which is generated during the melting process of bauxite
• very hard with good stamina and sharp edged for good
• abrasivity water unsoluble, no metallic particles, non conductive
• Used for most common anti corrosion works as removing of rust and old coatings where iron free blast material is necessary

Properties:

• squared grid form
• color black to brown
• hardness 9 Mohs
• density 4.0 kg/cmü
• cast weight 1.7 t/mü
• reuseable 10 - 30 times

minimum order amount 25 kg / price per kg up to 950 kg

iron containing, synthetic blast material

• hard cast granual material is made according to standard DIN.8201
• large hardness and grid sharpness for highest abrasive use
• water unsoluble
• used as blast material in blast cabins to remove old coatings and preparation for plating

Properties:

• squared grid
• gray clor
• hardness 61 - 65 HRC
• density 8.00 kg/dmü
• cast weight 3.8 t/mü
• reuseable 150 times

Call for Current prices!!

ironfree, natural blast material

• made of grinded nutshells ´
• low hardness and lieght weight
• no metallic parts, non conductive
• especially suitable for smooth surface cleaning and plastic deburring
• no particle removing of the blasted surface

Porperties:

• squared grid form
• brown color
• hardness 2.5 Mohs
• density 0.95 kg/l
• cast weight 0.72 t/mü

Minimum order amount 25 kg / for order up to 975 kg price / kg

iron free, synthetic blast material

• aluminum oxide with high purity degree which is generated during the melting process od bauxite
• Very hard, good stamina and sharp edged for exellent abrasivity
• water undoluble, no metallic particles
• Used for most common anti corrosion works as removing of rust and old coatings where iron free blast material is necessary

Properties:

• squared grid shape
• white color
• hardness 9 Mohs
• density 3.94 kg/cmü
• cast weight 1.7 t/mü
• reuseable 10 - 30 times

minimum order amount 25 kg / price per kg up to 950 kg

iron containing, synthetic blast material

• stainless steel balls are made of an alloy with a minimum content of carbon, sulphur, phosphorus and chrome with a special thermical treatment
• With the extended hardness and sharpness the material is used for extended abrasivity
• water insoluble
• used as blast material for cleaning and "shot peening" of stainless steel and non iron materials

Properties:

• round grid
• silver
• hardness 62 HRC
• density 7.40 kg/l
• cast weight 4.7 t/mü
• reuseable 100 times